Metallizing Wire
For your convenience, we have listed various industrial specifications applicable to our products. These specifications are intended as a reference only and not for determining, if required, Powder Alloy Corporation source approved products. We encourage you to CONTACT our customer service manager for specific Powder Alloy Corporation source approvals.
PAC Alloy # | Competitors Product | Application | Specification | Nominal Chemistry | |
---|---|---|---|---|---|
PAC 1000TI | Tafa 14T | Coating is used in aircraft engines and as an overlay for medical implants. | Carbon Hydrogen Iron Nitrogen Oxygen Titanium | 0.08 Max. 0.005 Max. 0.10 Max. 0.12 Max. 0.10 Max. Balance | |
PAC 912W | Tafa 74MXC | Coating is self bonding as general purpose, medium hardness, tough and wear resistant. | Aluminum Molybdenum Nickel | 7.25 6 80.0 Min. | |
PAC 909W | Metco 405
Tafa 79B | Coating is dense, high temperature and oxidation resistant. Bonds better than Molybdenum. | Aluminum Nickel | 17.0-27.0 Balance | |
PAC 908W | Tafa 73MXC | Coating is self bonding, high oxidation resistance and good machinability. | Aluminum Chrome Nickel | 17.0-27.0 18 70.0 Min. | |
PAC 906W | Tafa 75B | Coating is self bonding onto clean and smooth metallic surfaces. Coating is dense, tightly adherent and oxidation resistant. | Nickel Aluminum | 95 5 | |
PAC 718W | Tafa 78T | Coating is identical in chemistry to IN 718. High temperature resistance to a variety of acidic and chloride environments. Excellent oxidation resistance up to 1800 degrees Fahrenheit. | Aluminum Chrome ColumbiumA Iron Molybdenum Nickel Titanium APlus Tantalum | 0.5 19 32 Balance 3.05 5 0.95 | |
PAC 625W | Tafa 71T | Coating is identical in chemistry to IN 625. Used in applications requiring high temperature resistance to a variety of corrosive environments. | Aluminum Carbon Chromium Cobalt ColumbiumA Iron Manganese Molybdenum Nickel Silicon Sulfur Titanium APlus Tantalum | 0.40 Max. 0.10 Max. 20.0-23.0 if determined 3.15-4.15 5.0 Max. 0.50 Max. 8.0-10.0 Balance 0.50 Max. .015 Max. .040 Max. | |
PAC 600W | Metco Metcoloy 33 | A high machinable alloy suitable for wear and corrosion resistance. | Chrome Iron Nickel | 15.5 8 Balance | |
PAC 420W | Metco Metcoloy #2
Tafa 60T | A high Chromium Stainless Steel alloy that provides excellent wear qualities that corrosion resistance. | Carbon Chrome Iron Nickel Silicon | 0.35 13 Balance 0.5 0.5 | |
PAC 400W | Tafa 70T | Coating is a Montel deposit that exhibits corrosion and load bearing resistant surfaces particularly in seawater and caustic environments. Coating is easily machinable. | Aluminum Carbon Copper Iron Manganese Nickel Silicon Sulfur | 0.5 Max. 0.15 Max. 28.0-34.0 1.0-2.5 1.5 Max. Balance 0.5 Max. 0.2 Max. | |
PAC 276W | Metco 8276
Tafa 77T | Coating has excellent resistance to stress corrosion, cracking and chlorine environments through 1800 degrees Fahrenheit. | Chrome Iron Molybdenum Nickel Tungsten | 15.5 5.5 16 Balance 3.75 | |
PAC 308W | Tafa 80T | Coating is used as an overlay over a variety of 300 series Stainless. Moderate resistance to general corrosion, dimensional restoration and print rolls. | Carbon Chromium Copper Manganese Molybdenum Nickel Phosphorus Silicon Sulfur | 0.08 Max. 19.5-22.0 0.75 Max. 1.0-2.5 0.75 Max. 9.0-11.0 0.03 Max. 0.30-0.65 0.03 Max. | |
PAC 200W | Tafa 06T | Exhibiting protection at high temperatures, coating is beneficial as an overlay. | Nickel | 99.0 Min. | |
PAC 98W | Tafa 06C | Coating is bright and resistant to oxidation, corrosion and heat resistant. | Chrome Nickel | 20 80 | |
PAC 118W | Metco Spray Bond
Tafa 13T | Coating is beneficial for repair and salvage of automotive cracked blocks, heads and similar castings, mold patterns and latheways. | Molybdenum | 99.0 Min. | |
PAC 67W | Coating is dense, little to no porosity and low oxide content. Excellent for fretting wear applications. | Copper Iron Nickel | Balance 0.55 30.5 | ||
PAC 90W | Tafa TWX106 | Coating is identical in chemistry to Stellite 31. A cobalt base alloy having a very good stress rupture, endurance and creep properties. Good for oxidizing and reducing atmospheres to 2100 degrees Fahrenheit. | Carbon Chromium Cobalt Nickel Tungsten | 0.5 25.5 Balance 10.5 7.5 | |
PAC 30W | Tafa 30T | Mild Steel, Copper Coated | AWSE70S-6 | ||
PAC 16W | Metco Spray Bronze AA
Tafa 10T | Coating can be used as a bearing surface with excellent resistance to fretting, cavitational wear and for salvage and build up of brass and bronze surfaces. | Aluminum Copper Iron | 10 Balance 1.5 | |
PAC A13 | Metco Silvaloy A30
Tafa 30S | Coating can be easily machined. Used for aircraft engine seals. | Copper Silver Zink | 38 30 32 | |
PAC 10W | Metco Copper
Tafa 05T | Coating can replace brazing. Used in electrical applications. | Copper | 98.0 Min. | |
PAC 1100W | Metco Aluminum | Exhibits excellent electrical and heat conductivity. Produces dense, corrosion and oxidation resistant coatings. | Aluminum | 99.0 Min. | |
PAC 4043W | Metco Aluminum SF
Tafa OIS | Coatings are harder and slightly denser than PAC 1100W coatings. Used for repair of worn of mismachined Aluminum or Magnesium substrates. | Aluminum Silicon | Balance 5.25 |